TD-JS1 a high-strength polymer mortar, high strength polymer mortar Scope 1, wire rope plus a layer of polymer mortar pieces, stainless steel wire plaster. 2, the upper plate and beams of reinforced concrete bridges, piers and the central part of the main tower shaft. 3 insulation board plastering, corrosive gas corrosion of the plant reinforced concrete structures 4, building cracks, holes, peeling and other parts of reinforcement 5, wall, ceiling and roof insulation reinforced with fibers reinforced layer of polystyrene insulation board 6, Cellular concrete, holes, cracks and damage the protective layer leak repair tendons and other defects Second, product features high compressive strength, rapid curing, good adhesion properties; good water retention properties and crack resistance, high alkali resistance, ultraviolet light; easy to operate, can damp grass construction, green. Anti-aging: 3000 hours without the appearance of defects in a rapid test. Frost resistance: more than 300 freeze-thaw cycles without any exception. Peel: old and new interface combined with a solid, positive high tensile strength. Third, the technical indicators (performance standards: GB50367-2006) Specifications Model MPa compressive strength and flexural strength expansion MPa% MPa positive pull splitting tensile bond strength MPa Shear strength MPa 28d 28d TD-JS1 ≥12.2 ≥60 0.02 ≥7.5 ≥2 ≥12 Fourth, the construction method grassroots requirements and treatment:? primary surface should be smooth, rough, clean, no oil, no floating dust, there should be from the sand, hollowing, cracks and other phenomena. Construction of high-pressure water rinse before application and keep moist state, but may not have water. When the interfacial adhesion can be pre-painted high-strength polymer mortar interface treatment agent. ? Material preparation: A water material ratio is 10% -12% of the proportion of water mixed evenly, with a good slurry should guarantee used within 0.5-1 hours. ? Construction: concrete in the wet grass surface evenly coated over the first polymer mortar primer (powder: water weight ratio 3:1), while brushing the side wipe polymer mortar. TD-JS a high-strength polymer mortar construction area should not be too large, should be staggered slitting block construction, each area should not be greater than 10m2, construction staggered intervals of not less than 24 hours. Layered construction, the left seam position should be staggered with each other. ? TD-JS high-strength polymer mortar paving should be finished immediately after the water pressure and a smooth wiping, wiping pressure should not be repeated. In case of air bubbles should be punctured, the surface should be dense. Surface layer thickness of the top surface of the facade or greater than 10mm should be layered construction. Plastering thickness of each layer is preferably 5-10mm, pending before the lower layer can be carried out during the construction finger touch dry. ? Conservation: TD-JS after high-strength polymer mortar construction, surface means you should spray the conservation or covered straw mat, sacks kept moist touch dry after. Curing temperature did not end at 5 ℃. TD-JS high-strength polymer mortar 24 hours after application, cover with plastic sheeting and wet curing 7 days, when watering conditions can be timed to the surface. Fifth, packaging, storage 1, high-strength polymer mortar white plastic bags, packaging specifications 25kg / bag. 2, the product unopened, should be in a dry, cool, ventilated packaging at the store. Under normal storage and transport conditions, shelf life of 12 months.